利用对-硝基苯基重氮氟硼酸盐和聚酰胺酸进行重氮偶合反应,再经过酰亚胺化反应,合成了侧链含偶氮苯发色团的聚酰亚胺非线性光学材料(NLOPI)。在室温下测试了NLOPI的光致变色性能,研究了激光作用时间和激光功率密度对光致变色性能的影响。研究发现,在波长为532 nm的YAG激光作用下,随着激光辐射时间的延长和激光功率密度的增大,NLOPI在360 nm处的吸收增强,而在500 nm处的吸收减弱。采用单光束Z-扫描技术,系统地研究了NLOPI三阶非线性光学特性。研究表明,侧链含偶氮苯发色团的聚酰亚胺为自散焦介质,其非线性折射率n2为-1.62×10-7 esu,非线性折射系数γ为-4.04×10-14 m2/W,非线性吸收系数β为3.98×10-8 m/W,三阶光学非线性极化率χ(3)为3.41×10-18 m2/W。
材料 光致变色 非线性光学 聚酰亚胺 偶氮苯发色团 Z-扫描
西安交通大学电信学院光电技术与太阳能研究所,西安 710049
通过双醚化反应、氯甲基化反应以及在强碱性条件下进行的脱氯化氢反应制备聚(2-甲氧基-5-丁氧基)对苯乙炔(PMOBOPV)、聚(2-甲氧基-5-己氧基)对苯乙炔(PMOHOPV)、聚(2,5-二丁氧基)对苯乙炔(PDBOPV)和聚(2,5二己氧基)对苯乙炔(PDHOPV)等四种可溶性聚对苯乙炔(PPV)衍生物,通过紫外-可见吸收光谱对产物分子结构进行表征.结果显示,PMOBOPV、PMOHOPV、PDBOPV和PDHOPV的共轭π电子发生π→π*跃迁的吸收峰分别位于491 nm、495 nm、504 nm和510 nm处,相应的光学禁带宽度分别为2.23 eV、2.18 eV、2.12 eV和2.07 eV.利用简并四波混频技术测量PPV衍生物的三阶非线性光学性能,探讨了分子结构对PPV衍生物三阶非线性极化率(x(3))的影响.研究发现,激发波长为532nm时,PMOBOPV、PMOHOPV、PDBOPV和PDHOPV的共振x(3)值分别为3.45×10-10、5.13×10-10、7.15×10-10和9.61×10-10 esu;激发波长为1064 nm时,它们的非共振x(3)值分别为1.09×10-11、1.42×10-11、1.62×10-11和2.14×10-11 esu.
非线性光学 简并四波混频 聚对苯乙炔衍生物 三阶非线性极化率 Nonlinear optics Degenerate four-wave mixing Poly (ρ-phenylene vinylene) derivatives Third-order nonlinear optical susceptibility
1 School of Electron. and Inform. Eng., Xi’an Jiaotong University, Xi’an 710049, CHN
2 Dept. of Chem., Northwest University, Xi’an 710047, CHN
Solvatochromism Thermochromism Poly(32alkyl)thiophenes Photoluminescence spectra
Author Affiliations
Abstract
Institute of Photoelectric Technology and Solar Energy, School of Electrical and Information Engineer, Xi'an Jiaotong University, Xi'an 710049
A soluble poly(2-methoxy-5-decoxy)-p-phenylene vinylene (PMODOPV) was synthesized via dehydrochlorination reaction and characterized by UV-visible absorption spectrum. The results showed that PMODOPV had a broad optical absorption band in the range of 450---550 nm and the optical band gap was calculated to be around 2.12 eV. The third-order nonlinear optical susceptibilities (χ(3)) of PMODOPV films implanted by 30-keV N+ ions in the dose range of 3.8 * 10^(15)---9.6 * 10^(16) ions/cm2 were measured by degenerate four-wave mixing (DFWM) technique. The results demonstrated that the resonant and off-resonant χ(3) values were all enhanced significantly by means of ion implantation. The maximum resonant χ(3) value of 9.67 * 10^(-9) esu at 532 nm and off-resonant χ(3) value of 2.49 * 10^(-10) esu at 1.064 μm were obtained when the ion dose was 3.8 * 10^(16) ions/cm2.
160.4330 nonlinear optical materials 160.5470 polymers 250.2080 electro-optic polymers Chinese Optics Letters
2005, 3(9): 09539
1 Department of Electronic Science and Technolog Xi’an Jiaotong University,Xi’an 710049, China
2 Department of Applied Physics Xidian University, Xi’an 710071, China
3 Xi’an Institute of Optics and Precision Mechanics, The Chinese Academy of Sciences, Xi’an 710068, China
spatial soliton photorefractive-photovoltalic crystal screening soliton space-charge field Chinese Journal of Lasers B
2001, 10(3): 223